| Metal |
Nominal Composition |
Density (lbs/in^2) |
Elect. Conduct. (%IACS) |
Melting Temp Solidus
(F°) |
Annealing Temp (F°) |
Tensile Strength KSI
Annealed |
Tensile Strength KSI
Annealed |
% Elongation IN 2"
Annealed |
% Elongation IN 2"
Hard |
| Aluminum Alloy 1100 |
99.0 min Al |
.098 |
57.0 |
1215 |
650-775 |
13 |
24 |
35 |
5 |
| C10200 Copper |
99.95 min Cu |
.323 |
101.0 |
1981 |
700-1200 |
32 |
50 |
45 |
6 |
| C 19400 |
97.4Cu, 2.4Fe, .13Zn, .04P |
.322 |
65.0 |
1980 |
700-1200 |
45 |
67 |
32 |
4 |
| C21000 Gilding Metal |
95Cu, 5Zn |
.320 |
56.0 |
1920 |
800-1450 |
34 |
56 |
45 |
5 |
| C22000 Commercial Bronze |
90Cu, 10Zn |
.318 |
44.0 |
1870 |
800-1450 |
37 |
61 |
45 |
5 |
| C23000 Red Brass |
85Cu, 15Zn |
.316 |
37.0 |
1810 |
800-1350 |
39 |
70 |
48 |
5 |
| C24000 Low Brass |
80Cu, 20Zn |
.313 |
32.0 |
1770 |
800-1300 |
42 |
74 |
52 |
7 |
| C26000 Cartridge Brass |
70Cu, 30Zn |
.308 |
28.0 |
1680 |
800-1400 |
44 |
76 |
66 |
8 |
| C51000 Phosphor Bronze A |
94.8Cu, 5Sn, .2P |
.320 |
15.0 |
1750 |
900-1250 |
47 |
81 |
64 |
10 |
| C52100 Phosphor Bronze C |
91.8Cu, 8Sn, .2P |
.318 |
13.0 |
1620 |
900-1250 |
55 |
93 |
70 |
10 |
| C68800 |
73.5Cu, 22.7Zn, 3.4Al, .4Co |
.296 |
18.0 |
1740 |
750-1100 |
82 |
109 |
36 |
6 |
| C71500 Cupro-Nickel |
69.5Cu, 30Ni, .5Fe |
.323 |
4.6 |
2140 |
1200-1500 |
55 |
78 |
45 |
5 |
| C72500 |
88.2Cu, 9.5Ni, 2.3Sn |
.321 |
11.0 |
1940 |
1200-1475 |
55 |
83 |
35 |
3 |
| C75200 Nickel-Silver |
65Cu, 18Ni, 17Zn |
.316 |
6.0 |
1960 |
1100-1400 |
58 |
85 |
40 |
3 |
| C7025 High Performance Alloy |
Bal. Cu, 3.0Ni, .65Si, .15Mg |
.318
|
40.0
|
1967
|
Proprietary
|
90
|
125
|
10
|
5
|
| Beryllium Copper Alloys (T=Precipatation
heat Treated) |
|
|
|
|
|
|
|
| C17000 C17000T
|
98.3Cu, 1.7Be, Ni, Co, Fe |
.304
|
22.0
|
1590
|
1425-1475
|
70
165
|
110
190
|
45
7
|
5
3
|
| C17200 C17200T
|
98.1Cu, 1.9Be, Ni, Co, Fe |
.298
|
22.0
|
1590
|
1425-1475
|
70
175
|
110
200
|
45
6
|
5
2
|
| C17500 C17500T |
96.9Cu, 2.55Co, .55Be |
.311
|
45.0
|
1885
|
1675-1725
|
45
110 |
78
115 |
28
12 |
5
8 |
| Nickel 201 |
99.5Ni, .20Mn, .15Fe, .01C |
.321 |
22.5 |
2615 |
1300-1500 |
55 |
115 |
55 |
5 |
| Nickel 270 |
99.97Ni |
.321 |
23.5 |
2650 |
700-1200 |
50 |
90 |
50 |
5 |
| Monel 400 |
Bal. Ni, 31.5Cu, 1.1Fe, 1Mn, .2Si, .2C |
.319 |
3.3 |
2460 |
1400-1600 |
80 |
115 |
48 |
5 |
| Alloy 42 |
58.5Fe, 41.5Ni |
.293 |
2.5 |
2597 |
1400-1500 |
68 |
100 |
45 |
8 |
| Invar |
64Fe, 36Ni |
.291 |
2.0 |
2597 |
1380-1560 |
71 |
90 |
43 |
8 |
| ASTM F-15 Alloy |
54Fe, 29Ni, 17Co |
.302 |
3.5 |
2642 |
1200-1800 |
75 |
115 |
24 |
5 |
| Low Carbon Steel 1010 |
Bal. Fe, .45Mn, .1C |
.284 |
14.5 |
2750 |
1650-1750 |
48 |
85 |
36 |
7 |
| Stainless Steel Type 302 |
Bal. Fe, 18Cr, 9Ni, .15C max |
.290 |
2.4 |
2590 |
1850-2050 |
90 |
190 |
50 |
5 |
| Stainless Steel Type 304 |
Bal. Fe, 19Cr, 9.5Ni, .08C max |
.290 |
2.4 |
2650 |
1850-2050 |
85 |
185 |
50 |
4 |
| Stainless Steel Type 410 |
Bal. Fe, 12Cr, .15C |
.280 |
2.5 |
2790 |
1200-1600 |
70 |
180 |
25 |
15 |
| Stainless Steel Type 430 |
Bal. Fe, 17Cr, .12C |
.280 |
3.0 |
2750 |
1400-1525 |
75 |
110 |
25 |
10 |
| Inconel 600 |
72Ni, 15.5Cr, 8Fe, 1.0Mn, 0.5Si, Cu, Ti |
.306 |
10.9 |
2470 |
1700-1900 |
95 |
155 |
40 |
6 |
| Inconel 625 |
Bal. Ni, 21.5Cr, 9Mo, 5Fe, 3.65Nb |
.305 |
8.9 |
2460 |
2000-2200 |
115 |
180 |
42 |
12 |
*Solution heat treating temperature
|
|
|